From: Effect of elemental segregation and minor phase on mechanical properties of as-cast super-thick steels studied using in-situ synchrotron X-ray and neutron diffraction

$Effect of elemental segregation and minor phase on mechanical properties of as-cast super-thick steels studied using <i>in-situ</i> synchrotron X-ray and neutron diffraction$

Figure 2. Uniaxial tensile properties of the segregated (Q355) and non-segregated (Q370) samples. The Q355 samples exhibited significant reductions in yield strength, tensile strength, and elongation. Necking was observed in the Q370 samples, and the strain hardening rate was sustained over a longer strain range in the Q370 condition.